SEW 400 Grade X2CrNiMnMoNbN25-18-5-4 gedoofd (+Q)

-100,0 °C

206 GPa

20,0 °C

196 - 198 GPa

100,0 °C

190 - 193 GPa

200,0 °C

182 - 183 GPa

300,0 °C

174 - 175 GPa

400,0 °C

166 - 172 GPa

500,0 °C

158 - 159 GPa

600,0 °C

150 GPa

700,0 °C

142 GPa

800,0 °C

134 GPa

900,0 °C

127 GPa

1000,0 °C

120 GPa

20,0 °C

420 MPa

50,0 °C

400 MPa

100,0 °C

350 MPa

150,0 °C

310 MPa

200,0 °C

270 MPa

250,0 °C

255 MPa

300,0 °C

240 MPa

350,0 °C

225 MPa

400,0 °C

210 MPa

450,0 °C

210 MPa

500,0 °C

210 MPa

550,0 °C

200 MPa

20,0 °C

460 MPa

50,0 °C

435 MPa

100,0 °C

400 MPa

150,0 °C

355 MPa

200,0 °C

310 MPa

250,0 °C

290 MPa

300,0 °C

270 MPa

350,0 °C

255 MPa

400,0 °C

240 MPa

450,0 °C

240 MPa

500,0 °C

240 MPa

550,0 °C

230 MPa

-100,0 °C

1.49E-5 1/K

20,0 °C

1.61E-5 1/K

100,0 °C

1.58E-5 - 1.67E-5 1/K

200,0 °C

1.61E-5 - 1.72E-5 1/K

300,0 °C

1.65E-5 - 1.77E-5 1/K

400,0 °C

1.69E-5 - 1.81E-5 1/K

500,0 °C

1.73E-5 - 1.84E-5 1/K

600,0 °C

1.88E-5 1/K

700,0 °C

1.91E-5 1/K

800,0 °C

1.94E-5 1/K

900,0 °C

1.97E-5 1/K

1000,0 °C

2E-5 1/K

-100,0 °C

440 J/(kg·K)

20,0 °C

450 - 472 J/(kg·K)

100,0 °C

487 J/(kg·K)

200,0 °C

503 J/(kg·K)

300,0 °C

512 J/(kg·K)

400,0 °C

520 J/(kg·K)

500,0 °C

530 J/(kg·K)

600,0 °C

541 J/(kg·K)

700,0 °C

551 J/(kg·K)

800,0 °C

559 J/(kg·K)

900,0 °C

565 J/(kg·K)

1000,0 °C

571 J/(kg·K)

20,0 °C

11,9 - 12 W/(m·K)

100,0 °C

13,3 W/(m·K)

200,0 °C

15,1 W/(m·K)

300,0 °C

16,7 W/(m·K)

400,0 °C

18,3 W/(m·K)

500,0 °C

19,8 W/(m·K)

600,0 °C

21,3 W/(m·K)

700,0 °C

22,8 W/(m·K)

800,0 °C

24,3 W/(m·K)

900,0 °C

25,7 W/(m·K)

1000,0 °C

27,1 W/(m·K)

20,0 °C

3,3 mm²/s

100,0 °C

3,4 mm²/s

200,0 °C

3,7 mm²/s

300,0 °C

4,1 mm²/s

400,0 °C

4,3 mm²/s

500,0 °C

4,5 mm²/s

600,0 °C

4,7 mm²/s

700,0 °C

5 mm²/s

800,0 °C

5,4 mm²/s

900,0 °C

5,7 mm²/s

1000,0 °C

5,8 mm²/s