Roze bladen Grade 355.0 T71
Eigenschappen
Algemeen
| Eigendom | Waarde | Conditie |
|---|---|---|
| Dichtheid | 2,8 g/cm³ | T71 |
Mechanisch
| Eigendom | Temperatuur | Waarde | Conditie | Verwante normen | Vorm | Commentaar |
|---|---|---|---|---|---|---|
| Druksterkte vloeigrens | 248 MPa | T71 | ||||
| Elastische modulus | 76,0 GPa | T71 | ||||
| 25 °C | 70,3 GPa | T71 | ||||
| 150 °C | 67,6 GPa | T71 | ||||
| 204 °C | 64,1 GPa | T71 | ||||
| 260 °C | 56.5 GPa | T71 | ||||
| Verlenging | -195 °C | 1,5 % | T71 | Zandgegoten, rek in 50 mm | ||
| -80 °C | 1,5 % | T71 | Zandgegoten, rek in 50 mm | |||
| -28 °C | 1,5 % | T71 | Zandgegoten, rek in 50 mm | |||
| 1,5 % | T71 | |||||
| 24 °C | 1,5 % | T71 | Zandgegoten, rek in 50 mm | |||
| 100 °C | 2 % | T71 | Zandgegoten, rek in 50 mm | |||
| 150 °C | 3 % | T71 | Zandgegoten, rek in 50 mm | |||
| 205 °C | 8 % | T71 | Zandgegoten, rek in 50 mm | |||
| 260 °C | 16 % | T71 | Zandgegoten, rek in 50 mm | |||
| 315 °C | 36 % | T71 | Zandgegoten, rek in 50 mm | |||
| 371 °C | 50 % | T71 | Zandgegoten, rek in 50 mm | |||
| Vermoeidheidskracht | 70 MPa | T71 | voor 5x10⁸ cycli, R.R. Moore type test | |||
| Hardheid, Brinell | 75 [-] | T71 | 500 kg belasting, 10 mm b | |||
| 75,0 [-] | T71 | Roze bladen, ASTM B618 | Casten | |||
| 80,0 [-] | T71 | Roze bladen, ASTM B108 | Casten | |||
| Poisson-verhouding | 0,33 [-] | T71 | ||||
| Afschuifmodulus | 26,2 GPa | T71 | ||||
| Schuifsterkte | 241 MPa | T71 | ||||
| Treksterkte | -195 °C | 282 MPa | T71 | Zandgegoten | ||
| -80 °C | 255 MPa | T71 | Zandgegoten | |||
| -28 °C | 248 MPa | T71 | Zandgegoten | |||
| 200,0 MPa | T71 | |||||
| 205,0 MPa | T71 | Roze bladen, ASTM B618 | Casten | |||
| 235,0 MPa | T71 | Roze bladen, ASTM B108 | Casten | |||
| 24 °C | 240 MPa | T71 | Zandgegoten | |||
| 100 °C | 235 MPa | T71 | Zandgegoten | |||
| 150 °C | 207 MPa | T71 | Zandgegoten | |||
| 205 °C | 117 MPa | T71 | Zandgegoten | |||
| 260 °C | 67 MPa | T71 | Zandgegoten | |||
| 315 °C | 41 MPa | T71 | Zandgegoten | |||
| 371 °C | 25 MPa | T71 | Zandgegoten | |||
| Opbrengststerkte | -195 °C | 235 MPa | T71 | Zandgegoten, RP02 | ||
| -80 °C | 220 MPa | T71 | Zandgegoten, RP02 | |||
| -28 °C | 215 MPa | T71 | Zandgegoten, RP02 | |||
| 150,0 MPa | T71 | Roze bladen, ASTM B618 | Casten | RP02 | ||
| 185,0 MPa | T71 | Roze bladen, ASTM B108 | Casten | RP02 | ||
| 190,0 MPa | T71 | |||||
| 24 °C | 200 MPa | T71 | Zandgegoten, RP02 | |||
| 100 °C | 193 MPa | T71 | Zandgegoten, RP02 | |||
| 150 °C | 180 MPa | T71 | Zandgegoten, RP02 | |||
| 205 °C | 90 MPa | T71 | Zandgegoten, RP02 | |||
| 260 °C | 35 MPa | T71 | Zandgegoten, RP02 | |||
| 315 °C | 21 MPa | T71 | Zandgegoten, RP02 | |||
| 371 °C | 14 MPa | T71 | Zandgegoten, RP02 |
Thermisch
| Eigendom | Waarde | Conditie | Verwante normen | Vorm |
|---|---|---|---|---|
| Coëfficiënt van thermische uitzetting | 2.3e-05 1/K | T71 | ||
| Smeltpunt | 546,0 - 621,0 °C | T71 | Roze platen, ASTM B108, ASTM B618 | Casten |
| 560,0 °C | T71 | |||
| Specifieke warmtecapaciteit | 880,0 J/(kg·K) | T71 | ||
| Thermische geleidbaarheid | 160,0 W/(m·K) | T71 |
Elektrisch
| Eigendom | Waarde | Conditie | Commentaar |
|---|---|---|---|
| Elektrische geleidbaarheid | 20880000 S/m | T71 | Typische/afgeleide waarden |
| Specifieke elektrische geleidbaarheid | 36% GBCS | T71 | Typische waarden |
Chemische eigenschappen
| Eigendom | Waarde | Conditie | Verwante normen | Vorm |
|---|---|---|---|---|
| Aluminium | 90,3 - 94,1 % | T71 | ||
| Chroom | 0,25% | T71 | Roze platen, ASTM B108, ASTM B618 | Casten |
| Koper | 1,0 - 1,5 % | T71 | Roze platen, ASTM B108, ASTM B618 | Casten |
| Strijkijzer | 0,6 % | T71 | ||
| 0,60 % | T71 | Roze platen, ASTM B108, ASTM B618 | Casten | |
| Magnesium | 0,4 - 0,6 % | T71 | Roze platen, ASTM B108, ASTM B618 | Casten |
| Mangaan | 0,5 % | T71 | Roze platen, ASTM B108, ASTM B618 | Casten |
| Andere | 0,15 % | T71 | ||
| Silicium | 4,5 - 5,5 % | T71 | Roze platen, ASTM B108, ASTM B618 | Casten |
| Titanium | 0,25% | T71 | Roze platen, ASTM B108, ASTM B618 | Casten |
| Zink | 0,35 % | T71 | Roze platen, ASTM B108, ASTM B618 | Casten |
Metaal
- EN 573-3 klasse 3.0515 O3
- EN 573-3 kwaliteit AW-4043A O3
- EN 573-3 kwaliteit AW-4047A O3
- Roze bladen Grade 242.0 O
- EN 573-3 klasse AW-5556A F
- EN 573-3 kwaliteit AW-5556A O3
- EN 573-3 klasse AW-5087 F
- EN 573-3 kwaliteit AW-5087 O3
- Roze bladen Grade 319.0 T5
- EN 573-3 klasse AW-1110 F
- Roze bladen Grade 201.0 T7