AA 5052-O Aluminium: Uitstekende Corrosieweerstand en Lasbaarheid
Overzicht van AA 5052-O Aluminium
Aluminiumlegering AA 5052 is een niet-warmtebehandelbare legering met uitstekende afwerkingskwaliteiten. Deze legering biedt superieure corrosieweerstand vergeleken met de meeste aluminiumlegeringen, met name tegen zoutwater en mariene atmosferische condities. AA 5052 kan gemakkelijk worden gelast met de meest voorkomende lastechnieken en bezit een van de beste laskenmerken van alle aluminiumlegeringen.
Eigenschappen
Algemene Eigenschappen
| Eigenschap | Waarde | Toestand | Gerelateerde Normen |
|---|---|---|---|
| Dichtheid | 2,68 g/cm³ | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
Mechanische Eigenschappen
| Eigenschap | Waarde | Toestand | Gerelateerde Normen | Opmerking |
|---|---|---|---|---|
| Buigmoeheidsterkte | 110,0 MPa | O | AA Standards | |
| Elasticiteitsmodulus | 70,0 GPa | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | |
| Hardheid, Brinell | 47,0 HB | O | AA Standards | |
| Vlakke-staat-barstingszwaarte | 22,0 - 35,0 MPa·√m | Typisch voor gesmede 5000-serie aluminium | ||
| Getal van Poisson | 0,33 | Typisch voor gesmede 5000-serie aluminium | ||
| Schuifmodulus | 26,0 - 26,5 GPa | Typisch voor gesmede 5000-serie aluminium | ||
| Treksterkte | 170,0 - 215,0 MPa | O | AA Standards, ASTM B209, ASTM B313, ASTM B547 | |
| Treksterkte | 170,0 - 240,0 MPa | O | AA Standards, ASTM B210, ASTM B221, ASTM B241 | |
| Treksterkte | 170,0 - 220,0 MPa | O | AA Standards, ASTM B211 | |
| Treksterkte | 170,0 MPa | O | AA Standards, ASTM B483 | |
| Treksterkte | 195,0 MPa | O | AA Standards | |
| Treksterkte | 220,0 MPa | O | AA Standards, ASTM B316 |
Thermische Eigenschappen
| Eigenschap | Temperatuur | Waarde | Toestand | Gerelateerde Normen | Opmerking |
|---|---|---|---|---|---|
| Uitzettingscoëfficiënt | 20 °C | 2,38e-05 1/K | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | |
| Uitzettingscoëfficiënt | 100 °C | 2,38e-05 1/K | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | |
| Maximale diensttemperatuur | 150,0 °C | Typisch voor gesmede 5000-serie aluminium | |||
| Smeltpunt | 605,0 - 650,0 °C | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | ||
| Specifieke warmtecapaciteit | 879,0 - 963,0 J/(kg·K) | Typisch voor gesmede 5000-serie aluminium | |||
| Warmtegeleiding | 138 W/(m·K) | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
Elektrische Eigenschappen
| Eigenschap | Waarde | Toestand | Gerelateerde Normen |
|---|---|---|---|
| Elektrische geleidbaarheid | 20.000.000 S/m | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
| Elektrische weerstand | 5e-08 Ω·m | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
Chemische Samenstelling
| Element | Waarde (% gewicht) | Toestand | Gerelateerde Normen |
|---|---|---|---|
| Chroom | 0,15 - 0,35 | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
| Koper | 0,1 | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
| IJzer | 0,40 | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
| Magnesium | 2,2 - 2,8 | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
| Mangaan | 0,1 | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
| Silicium | 0,25 | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
| Zink | 0,1 | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
Technologische Eigenschappen
| Eigenschap | Beoordeling |
|---|---|
| Harden | Beperkt hardbaar |
| Corrosie-eigenschappen | Spanningscorrosiebarsting: geen schade tijdens bedrijf en laboratoriumtests; algemeen: zeer goed, zonder bescherming in industriële of zeewateratmosfeer |
| Algemene bewerkbaarheid | Algemeen: slecht (O, H32), voldoende (H34, H36, H38) |
| Vormbaarheid | Algemeen (toestand): goed (O), acceptabel (H32, H34), slecht (H36, H38) |
EN 573-3 AW-5052 H48 – Superieure Corrosiebestendige Aluminiumlegering voor Maritieme Toepassingen
AA 5052 H32 Aluminiumlegering: Superieure Corrosieweerstand en Lasprestaties
Metaal
- AA Kwaliteit 5456 O Aluminium Standaard – Belangrijkste Mechanische Eigenschappen
- AA 5083-O Aluminiumlegering Standaard – Hoge Sterkte & Corrosieweerstand
- AA Standaarden Kwaliteit 6066 T6 Aluminiumlegering Specificaties
- AA 6351 T6 aluminiumlegering – Technische standaarden en eigenschappen
- AA Normen Graad 5454 O – Uitgebreide Aluminiumlegering Specificatie
- AA Standaarden Graad 1060 O – Complete Materiaalspecificaties & Normen
- AA 3004 O: Uitgebreide Eigenschappen & Prestatieoverzicht
- AA 5050O Aluminiumlegering – Normen & Mechanische Eigenschappen
- AA Standaard Kwaliteit 5154 O: Belangrijkste Mechanische Eigenschappen & Specificaties
- AA 7178 T6: Hoogsterkte Magnesium-Koperlegering voor Geavanceerde Metalbewerking
- AA 6063 T4 Aluminium – Premium Architecturaal Legering met Uitzonderlijke Corrosieweerstand