AA-normen Grade 5456 O
Eigenschappen
Algemeen
| Eigendom | Waarde | Conditie | Verwante normen |
|---|---|---|---|
| Dichtheid | 2,66 g/cm³ | O | AA-normen, ASTM B209, ASTM B210, ASTM B221, ASTM B241 |
Mechanisch
| Eigendom | Waarde | Conditie | Verwante normen | Commentaar |
|---|---|---|---|---|
| Elastische modulus | 71,0 GPa | O | AA-normen, ASTM B209, ASTM B210, ASTM B221, ASTM B241 | |
| Plane-Strain Fracture Toughnes | 22,0 - 35,0 MPa·√m | Typisch voor gesmeed aluminium uit de 5000-serie | ||
| Poisson-verhouding | 0,33 [-] | Typisch voor gesmeed aluminium uit de 5000-serie | ||
| Afschuifmodulus | 26,0 - 26,5 GPa | Typisch voor gesmeed aluminium uit de 5000-serie | ||
| Treksterkte | 265,0 MPa | O | AA-normen, ASTM B209 | |
| 270,0 MPa | O | AA-normen, ASTM B209 | ||
| 275,0 MPa | O | AA-normen, ASTM B209 | ||
| 285,0 - 360,0 MPa | O | AA-normen, ASTM B209 | ||
| 285,0 - 365,0 MPa | O | AA-normen, ASTM B210, ASTM B221, ASTM B241 | ||
| 290,0 - 365,0 MPa | O | AA-normen, ASTM B209 | ||
| 310,0 MPa | O | AA-normen |
Thermisch
| Eigendom | Temperatuur | Waarde | Conditie | Verwante normen | Commentaar |
|---|---|---|---|---|---|
| Coëfficiënt van thermische uitzetting | 20 °C | 2.3899999999999998e-05 1/K | O | AA-normen, ASTM B209, ASTM B210, ASTM B221, ASTM B241 | |
| 100 °C | 2.3899999999999998e-05 1/K | O | AA-normen, ASTM B209, ASTM B210, ASTM B221, ASTM B241 | ||
| Maximale servicetemperatuur | 150,0 °C | Typisch voor gesmeed aluminium uit de 5000-serie | |||
| Smeltpunt | 570,0 - 640,0 °C | O | AA-normen, ASTM B209, ASTM B210, ASTM B221, ASTM B241 | ||
| Specifieke warmtecapaciteit | 879,0 - 963,0 J/(kg·K) | Typisch voor gesmeed aluminium uit de 5000-serie | |||
| Thermische geleidbaarheid | 117.0 | O | AA-normen, ASTM B209, ASTM B210, ASTM B221, ASTM B241 |
Elektrisch
| Eigendom | Waarde | Conditie | Verwante normen |
|---|---|---|---|
| Elektrische geleidbaarheid | 17000000,0 S/m | O | AA-normen, ASTM B209, ASTM B210, ASTM B221, ASTM B241 |
| Elektrische weerstand | 5.88e-08 ·m | O | AA-normen, ASTM B209, ASTM B210, ASTM B221, ASTM B241 |
Chemische eigenschappen
| Eigendom | Waarde | Conditie | Verwante normen |
|---|---|---|---|
| Chroom | 0,05 - 0,2 % | O | AA-normen, ASTM B209, ASTM B210, ASTM B221, ASTM B241 |
| Koper | 0,1 % | O | AA-normen, ASTM B209, ASTM B210, ASTM B221, ASTM B241 |
| Strijkijzer | 0,40 % | O | AA-normen, ASTM B209, ASTM B210, ASTM B221, ASTM B241 |
| Magnesium | 4,7 - 5,5 % | O | AA-normen, ASTM B209, ASTM B210, ASTM B221, ASTM B241 |
| Mangaan | 0,5 - 1,0 % | O | AA-normen, ASTM B209, ASTM B210, ASTM B221, ASTM B241 |
| Silicium | 0,25% | O | AA-normen, ASTM B209, ASTM B210, ASTM B221, ASTM B241 |
| Titanium | 0,2 % | O | AA-normen, ASTM B209, ASTM B210, ASTM B221, ASTM B241 |
| Zink | 0,25% | O | AA-normen, ASTM B209, ASTM B210, ASTM B221, ASTM B241 |
Technologische eigenschappen
| Eigenschap | ||
|---|---|---|
| Hardsolderen | algemeen:er is geen hardsolderen bekend of ontwikkeld
| |
| Corrosie-eigenschappen | Spanningscorrosie:geen schade tijdens bedrijf, beperkte schade tijdens laboratoriumtests, algemeen:zeer goed, zonder bescherming in industriële of zeewateratmosfeer
| |
| Algemene bewerkbaarheid | Algemeen:slecht (O, H321, H116)
| |
| Werkbaarheid | algemeen (conditie):acceptabel (O), slecht (H321, H116)
| |
Metaal