AA-normen Grade 6351 T6
Eigenschappen
Algemeen
| Eigendom | Waarde | Conditie | Verwante normen |
|---|---|---|---|
| Dichtheid | 2,71 g/cm³ | T6 | AA-normen, ASTM B221, ASTM B241, ASTM B345 |
Mechanisch
| Eigendom | Waarde | Conditie | Verwante normen | Commentaar |
|---|---|---|---|---|
| Buigen Vermoeidheid Kracht | 90,0 MPa | T6 | AA-normen | |
| Elastische modulus | 69,0 GPa | T6 | AA-normen, ASTM B221, ASTM B241, ASTM B345 | |
| Hardheid, Brinell | 95,0 [-] | T6 | AA-normen | |
| Plane-Strain Fracture Toughnes | 22,0 - 35,0 MPa·√m | Typisch voor gesmeed aluminium uit de 6000-serie | ||
| Poisson-verhouding | 0,33 [-] | Typisch voor gesmeed aluminium uit de 6000-serie | ||
| Afschuifmodulus | 26,0 - 26,5 GPa | Typisch voor gesmeed aluminium uit de 6000-serie | ||
| Treksterkte | 290,0 MPa | T6 | AA-normen, ASTM B221, ASTM B241, ASTM B345 | |
| 310,0 MPa | T6 | AA-normen |
Thermisch
| Eigendom | Temperatuur | Waarde | Conditie | Verwante normen | Commentaar |
|---|---|---|---|---|---|
| Coëfficiënt van thermische uitzetting | 20 °C | 2.3399999999999996e-05 1/K | T6 | AA-normen, ASTM B221, ASTM B241, ASTM B345 | |
| 100 °C | 2.3399999999999996e-05 1/K | T6 | AA-normen, ASTM B221, ASTM B241, ASTM B345 | ||
| Smeltpunt | 555,0 - 650,0 °C | T6 | AA-normen, ASTM B221, ASTM B241, ASTM B345 | ||
| Specifieke warmtecapaciteit | 887,0 - 963,0 J/(kg·K) | Typisch voor gesmeed aluminium uit de 6000-serie | |||
| Thermische geleidbaarheid | 176 W/(m·K) | T6 | AA-normen, ASTM B221, ASTM B241, ASTM B345 |
Elektrisch
| Eigendom | Waarde | Conditie | Verwante normen |
|---|---|---|---|
| Elektrische geleidbaarheid | 27000000,0 S/m | T6 | AA-normen, ASTM B221, ASTM B241, ASTM B345 |
| Elektrische weerstand | 3.7e-08 Ω·m | T6 | AA-normen, ASTM B221, ASTM B241, ASTM B345 |
Chemische eigenschappen
| Eigendom | Waarde | Conditie | Verwante normen |
|---|---|---|---|
| Koper | 0,1 % | T6 | AA-normen, ASTM B221, ASTM B241, ASTM B345 |
| Strijkijzer | 0,50 % | T6 | AA-normen, ASTM B221, ASTM B241, ASTM B345 |
| Magnesium | 0,4 - 0,8 % | T6 | AA-normen, ASTM B221, ASTM B241, ASTM B345 |
| Mangaan | 0,4 - 0,8 % | T6 | AA-normen, ASTM B221, ASTM B241, ASTM B345 |
| Silicium | 0,7 - 1,3% | T6 | AA-normen, ASTM B221, ASTM B241, ASTM B345 |
| Titanium | 0,2 % | T6 | AA-normen, ASTM B221, ASTM B241, ASTM B345 |
| Zink | 0,2 % | T6 | AA-normen, ASTM B221, ASTM B241, ASTM B345 |
Technologische eigenschappen
| Eigenschap | ||
|---|---|---|
| Hardsolderen | algemeen:beperkt hardsolderen
| |
| Corrosie-eigenschappen | algemeen:zeer goed, zonder bescherming in industriële of zeewateratmosfeer
| |
| Algemene bewerkbaarheid | Algemeen:voldoende
| |
| Werkbaarheid | algemeen (voorwaarde):mit Mängel
| |