AA 1100-O Aluminiumlegering – Zuiverste Kwaliteit met Superieure Corrosiebestendigheid
AA 1100 is een zachte, niet-warmtebehandelbare legering met lage sterkte die uitstekende corrosiebestendigheid biedt. Met een samenstelling van 99% aluminium en 0,12% koper is AA 1100 de commercieel beschikbare zuiverste aluminiumlegering.
Eigenschappen
Algemeen
| Eigenschap | Waarde | Toestand | Gerelateerde Normen |
|---|---|---|---|
| Dichtheid | 2,71 g/cm³ | O (geglost) | AA Standaarden, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
Mechanisch
| Eigenschap | Waarde | Toestand | Gerelateerde Normen | Opmerking |
|---|---|---|---|---|
| Buigmoeheidsterkte | 35,0 MPa | O | AA Standaarden | |
| Elasticiteitsmodulus | 69,0 GPa | O | AA Standaarden, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | |
| Hardheid, Brinell | 23,0 | O | AA Standaarden | |
| Vlakke-trekbarstingstoughness | 22,0 - 35,0 MPa·√m | Typisch voor gewalste 1000-series aluminium | ||
| Poissonverhouding | 0,33 | Typisch voor gewalste 1000-series aluminium | ||
| Schuifmodulus | 25,9 GPa | Typisch voor gewalste 1000-series aluminium | ||
| Treksterkte | 75,0 - 105,0 MPa | O | AA Standaarden, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B547 | |
| Treksterkte (min) | 75,0 MPa | O | AA Standaarden, ASTM B483 | |
| Treksterkte (gemiddeld) | 90,0 MPa | O | AA Standaarden | |
| Treksterkte (ASTM B316) | 110,0 MPa | O | AA Standaarden, ASTM B316 |
Thermisch
| Eigenschap | Temperatuur | Waarde | Toestand | Gerelateerde Normen | Opmerking |
|---|---|---|---|---|---|
| Thermische uitdijtingscoëfficiënt | 20 °C | 2,36e-05 1/K | O | AA Standaarden, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | |
| Thermische uitdijtingscoëfficiënt | 100 °C | 2,36e-05 1/K | O | AA Standaarden, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | |
| Smeltpunt | 640,0 - 655,0 °C | O | AA Standaarden, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | ||
| Specifieke warmtecapaciteit | 900,0 - 963,0 J/(kg·K) | Typisch voor gewalste 1000-series aluminium | |||
| Thermische geleiding | 218,0 - 222,0 W/(m·K) | O | AA Standaarden, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
Elektrisch
| Eigenschap | Waarde | Toestand | Gerelateerde Normen |
|---|---|---|---|
| Elektrische geleiding | 33.000.000 - 34.000.000 S/m | O | AA Standaarden, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
| Elektrische weerstand | 2,94e-08 - 3,03e-08 Ω·m | O | AA Standaarden, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
Chemische samenstelling
| Element | Waarde | Toestand | Gerelateerde Normen |
|---|---|---|---|
| Aluminium | 99,0% | O | AA Standaarden, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
| Koper | 0,05 - 0,2% | O | AA Standaarden, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
| Mangaan | 0,05% | O | AA Standaarden, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
| Zink | 0,1% | O | AA Standaarden, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
Technologische eigenschappen
| Eigenschap | Details |
|---|---|
| Harden | Algemeen: mogelijk met commerciële processen en methoden |
| Corrosie-eigenschappen | Spanningscorrosiebarsting: geen schade tijdens bedrijf en laboratoriumtesten; algemeen: zeer goed, zonder bescherming in industriële of zeewateratmosfeer |
| Algemeen bewerkbaarheid | Algemeen: niet geschikt (O, H12), slecht (H14, H16, H18) |
| Vormbaarheid | Algemeen (toestand): goed (O, H12, H14), acceptabel (H16), slecht (H18) |
AA 1100 H18 Aluminiumlegering – Premiumkwaliteit 1100 met Superieure Corrosiebestendigheid
AA 2011 T8 Aluminiumlegering – Normen & Eigenschappen
Metaal
- ASTM B316 Kwaliteit 1100 O Aluminiumlegering – Superieure Corrosiebestendigheid & Zuiverste 1000-serie
- ASTM B483 Grade 1100 O Aluminium: Zuiver, Corrosieweerstand, Lage Sterkte
- ASTM B210 Grade 1100 O (Zacht Gegloeid) Aluminiumlegering – Maximale Vormbaarheid
- AA Kwaliteit 5456 O Aluminium Standaard – Belangrijkste Mechanische Eigenschappen
- AA 5083-O Aluminiumlegering Standaard – Hoge Sterkte & Corrosieweerstand
- AA Standaarden Kwaliteit 6066 T6 Aluminiumlegering Specificaties
- AA 6351 T6 aluminiumlegering – Technische standaarden en eigenschappen
- ASTM B211 Graad 1100 O Aluminiumlegering – Hoge Corrosiebestendigheid & Zuiverheid
- ASTM B241 Graad 1100 O Aluminium – Superieure Corrosieweerstand & Lage-Sterkte Legering
- AA Normen Graad 5454 O – Uitgebreide Aluminiumlegering Specificatie
- AA Standaarden Graad 1060 O – Complete Materiaalspecificaties & Normen