AA-normen Grade 6061 T4
AA 6061 is een gemakkelijk verkrijgbare legering met een goede oppervlakteafwerking en het vermogen om te worden geanodiseerd. Gemakkelijk te lassen en te solderen met een mooie oppervlakteafwerking. Weerstand tegen corrosie door zeewater en atmosferische omstandigheden. Geschikt voor warm smeden.
Eigenschappen
Algemeen
| Eigendom | Waarde | Conditie | Verwante normen |
|---|---|---|---|
| Dichtheid | 2,7 g/cm³ | T4 | AA-normen, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 |
Mechanisch
| Eigendom | Waarde | Conditie | Verwante normen | Commentaar |
|---|---|---|---|---|
| Buigen Vermoeidheid Kracht | 95,0 MPa | T4 | AA-normen | |
| Elastische modulus | 69,0 GPa | T4 | AA-normen, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 | |
| Hardheid, Brinell | 65.0 [-] | T4 | AA-normen | |
| Plane-Strain Fracture Toughnes | 22,0 - 35,0 MPa·√m | Typisch voor gesmeed aluminium uit de 6000-serie | ||
| Poisson-verhouding | 0,33 [-] | Typisch voor gesmeed aluminium uit de 6000-serie | ||
| Afschuifmodulus | 26,0 - 26,5 GPa | Typisch voor gesmeed aluminium uit de 6000-serie | ||
| Treksterkte | 180,0 MPa | T4 | AA-normen, ASTM B221, ASTM B241, ASTM B345 | |
| 205,0 MPa | T4 | AA-normen, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B483, ASTM B547 | ||
| 240,0 MPa | T4 | AA-normen |
Thermisch
| Eigendom | Temperatuur | Waarde | Conditie | Verwante normen | Commentaar |
|---|---|---|---|---|---|
| Coëfficiënt van thermische uitzetting | 20 °C | 2.36e-05 1/K | T4 | AA-normen, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 | |
| 100 °C | 2.36e-05 1/K | T4 | AA-normen, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 | ||
| Smeltpunt | 580,0 - 650,0 °C | T4 | AA-normen, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 | ||
| Specifieke warmtecapaciteit | 887,0 - 963,0 J/(kg·K) | Typisch voor gesmeed aluminium uit de 6000-serie | |||
| Thermische geleidbaarheid | 155,0 - 180,0 W/(m·K) | T4 | AA-normen, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 |
Elektrisch
| Eigendom | Waarde | Conditie | Verwante normen |
|---|---|---|---|
| Elektrische geleidbaarheid | 23000000,0 - 27000000,0 S/m | T4 | AA-normen, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 |
| Elektrische weerstand | 3.7e-08 - 4.35e-08 ·m | T4 | AA-normen, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 |
Chemische eigenschappen
| Eigendom | Waarde | Conditie | Verwante normen |
|---|---|---|---|
| Chroom | 0,04 - 0,35 % | T4 | AA-normen, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 |
| Koper | 0,15 - 0,4 % | T4 | AA-normen, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 |
| Strijkijzer | 0,70 % | T4 | AA-normen, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 |
| Magnesium | 0,8 - 1,2 % | T4 | AA-normen, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 |
| Mangaan | 0,15 % | T4 | AA-normen, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 |
| Silicium | 0,4 - 0,8 % | T4 | AA-normen, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 |
| Titanium | 0,15 % | T4 | AA-normen, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 |
| Zink | 0,25% | T4 | AA-normen, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 |
Technologische eigenschappen
| Eigenschap | ||
|---|---|---|
| Hardsolderen | algemeen:mogelijk met commerciële processen en methoden
| |
| Corrosie-eigenschappen | Spanningscorrosie:geen schade tijdens bedrijf en laboratoriumtests (O, T6, T651, T652, T6510, T6511), geen schade tijdens bedrijf, beperkte schade tijdens laboratoriumtests (T4, T451, T4510, T4511), algemeen:goed, zonder bescherming in industriële of zeewateratmosfeer
| |
| Algemene bewerkbaarheid | Algemeen:slecht (O), voldoende (T4, T451, T4510, T4511, T6, T651, T652, T6510, T6511)
| |
| Werkbaarheid | algemeen (conditie):goed (O), acceptabel (T4, T451, T4510, T4511), slecht (T6, T651, T652, T6510, T6511)
| |
Metaal