Roze bladen Grade 201.0 T6
Eigenschappen
Algemeen
| Eigendom | Waarde | Conditie |
|---|---|---|
| Dichtheid | 3,1 g/cm³ | T6 |
Mechanisch
| Eigendom | Waarde | Conditie | Verwante normen | Vorm | Commentaar |
|---|---|---|---|---|---|
| Charpy slagenergie, V-inkeping | 5,0 - 15,0 J | T6 | |||
| Elastische modulus | 71,0 GPa | T6 | |||
| 71 GPa | T6 | ||||
| Verlenging | 4,0 % | T6 | Roze bladen, ASTM B618 | Casten | A100 |
| 7,2 % | T6 | ||||
| 8 % | T6 | Zandgegoten, rek in 50 mm | |||
| Hardheid, Brinell | 135 [-] | T6 | 500 kg belasting, 10 mm b | ||
| Poisson-verhouding | 0,33 [-] | T6 | |||
| Afschuifmodulus | 23,0 GPa | T6 | |||
| Treksterkte | 415,0 MPa | T6 | Roze bladen, ASTM B618 | Casten | |
| 448 MPa | T6 | Zandgegoten | |||
| 460,0 MPa | T6 | ||||
| Opbrengststerkte | 345,0 MPa | T6 | Roze bladen, ASTM B618 | Casten | RP02 |
| 379 MPa | T6 | Zandgegoten, RP02 | |||
| 400,0 MPa | T6 |
Thermisch
| Eigendom | Temperatuur | Waarde | Conditie | Verwante normen | Vorm | Commentaar |
|---|---|---|---|---|---|---|
| Coëfficiënt van thermische uitzetting | 2.1e-05 1/K | T6 | ||||
| 100 °C | 0.0000193 1/K | T6 | niet-vermelde waarde tussen 20°C en de genoemde temperatuur | |||
| 200 °C | 0.0000227 1/K | T6 | niet-vermelde waarde tussen 20°C en de genoemde temperatuur | |||
| 300 °C | 0.0000247 1/K | T6 | niet-vermelde waarde tussen 20°C en de genoemde temperatuur | |||
| Smeltpunt | 570,0 °C | T6 | ||||
| 571,0 - 649,0 °C | T6 | Roze bladen, ASTM B618 | Casten | |||
| Specifieke warmtecapaciteit | 920,0 J/(kg·K) | T6 | ||||
| Thermische geleidbaarheid | 120,0 W/(m·K) | T6 |
Elektrisch
| Eigendom | Waarde | Conditie | Commentaar |
|---|---|---|---|
| Elektrische geleidbaarheid | 16000000,0 - 19000000,0 S/m | T6 | Typische/afgeleide waarden |
| Elektrische weerstand | 5.4e-08 - 6.4e-08 ·m | T6 | Typische waarden |
| Specifieke elektrische geleidbaarheid | 27,0 - 32,0 % GBCS | T6 | Typische waarden |
Chemische eigenschappen
| Eigendom | Waarde | Conditie | Verwante normen | Vorm |
|---|---|---|---|---|
| Aluminium | 92,1 - 95,1 % | T6 | ||
| Koper | 4,0 - 5,2 % | T6 | Roze bladen, ASTM B618 | Casten |
| Strijkijzer | 0,15 % | T6 | ||
| 0,15 % | T6 | Roze bladen, ASTM B618 | Casten | |
| Magnesium | 0,15 - 0,55% | T6 | Roze bladen, ASTM B618 | Casten |
| Mangaan | 0,2 - 0,5 % | T6 | Roze bladen, ASTM B618 | Casten |
| Andere | 0,1 % | T6 | ||
| Silicium | 0,1 % | T6 | Roze bladen, ASTM B618 | Casten |
| Zilver | 0,4 - 1,0 % | T6 | Roze bladen, ASTM B618 | Casten |
| Titanium | 0,15 - 0,35 % | T6 | Roze bladen, ASTM B618 | Casten |
Metaal
- ASTM A514 Rang F
- EN 1652 kwaliteit CuCo1Ni1Be TH
- EN 12163 Kwaliteit CuZr TH
- ASTM A666 Grade 201 gegloeid; Typ 201-2
- ASTM A666 Grade 201 gegloeid; Typ 201-1
- EN 12163 Kwaliteit CuBe2 M
- EN 12163 Kwaliteit CuZn10 M
- EN 12163 Kwaliteit CuZn40 M
- EN 12163 Kwaliteit CuZn33 M
- EN 10305-5 klasse St 33
- AA 201.0 T4