WL 3.2364 kwaliteit 3.2364 T5
Zeer goed lasbaar gietmateriaal met zeer goede gieteigenschappen. Gietstukken zijn gevoelig voor stootbelastingen.Toepassing:fittingen
Eigenschappen
Algemeen
| Eigendom | Temperatuur | Waarde | Conditie | Verwante normen |
|---|---|---|---|---|
| Dichtheid | 20,0 °C | 2,7 g/cm³ | T5 | WL 3.2364 |
Mechanisch
| Eigendom | Temperatuur | Waarde | Conditie | Verwante normen | Commentaar |
|---|---|---|---|---|---|
| Elastische modulus | 20,0 °C | 70,6 GPa | T5 | WL 3.2364 | |
| Verlenging | 20,0 °C | 1,0 % | T5 | WL 3.2364 | |
| 20,0 °C | 3,0 % | T5 | WL 3.2364 | ||
| 24,0 °C | 3,5 % | T5 | WL 3.2364 | A50 | |
| 24,0 °C | 5,0 % | T5 | WL 3.2364 | A50 | |
| 100,0 °C | 4,0 % | T5 | WL 3.2364 | A50 | |
| 100,0 °C | 6,0 % | T5 | WL 3.2364 | A50 | |
| 149,0 °C | 5,0 % | T5 | WL 3.2364 | A50 | |
| 149,0 °C | 10,0 % | T5 | WL 3.2364 | A50 | |
| 204,0 °C | 15,0 % | T5 | WL 3.2364 | A50 | |
| 204,0 °C | 30,0 % | T5 | WL 3.2364 | A50 | |
| 260,0 °C | 30,0 % | T5 | WL 3.2364 | A50 | |
| 260,0 °C | 55,0 % | T5 | WL 3.2364 | A50 | |
| 316,0 °C | 60,0 % | T5 | WL 3.2364 | A50 | |
| 316,0 °C | 70,0 % | T5 | WL 3.2364 | A50 | |
| 371,0 °C | 75,0 % | T5 | WL 3.2364 | A50 | |
| 371,0 °C | 80,0 % | T5 | WL 3.2364 | A50 | |
| Hardheid, Brinell | 20,0 °C | 70.0 [-] | T5 | WL 3.2364 | |
| 20,0 °C | 75,0 [-] | T5 | WL 3.2364 | ||
| 20,0 °C | 80,0 [-] | T5 | WL 3.2364 | ||
| Poisson-verhouding | 0,33 [-] | Typisch voor gegoten aluminium uit de 3xx.x-serie | |||
| Afschuifmodulus | 2,8 GPa | Typisch voor gegoten aluminium uit de 3xx.x-serie | |||
| Schuifsterkte | 20,0 °C | 177,0 MPa | T5 | WL 3.2364 | |
| Treksterkte | 20,0 °C | 167.0 MPa | T5 | WL 3.2364 | |
| 20,0 °C | 177,0 MPa | T5 | WL 3.2364 | ||
| 20,0 °C | 216,0 MPa | T5 | WL 3.2364 | ||
| 20,0 °C | 235,0 MPa | T5 | WL 3.2364 | ||
| 24,0 °C | 226,0 MPa | T5 | WL 3.2364 | ||
| 24,0 °C | 265,0 MPa | T5 | WL 3.2364 | ||
| 100,0 °C | 206,0 MPa | T5 | WL 3.2364 | ||
| 149,0 °C | 147,0 MPa | T5 | WL 3.2364 | ||
| 149,0 °C | 157,0 MPa | T5 | WL 3.2364 | ||
| 204,0 °C | 82,0 MPa | T5 | WL 3.2364 | ||
| 260,0 °C | 52,0 MPa | T5 | WL 3.2364 | ||
| 316,0 °C | 27,0 MPa | T5 | WL 3.2364 | ||
| 371,0 °C | 18,0 MPa | T5 | WL 3.2364 |
Thermisch
| Eigendom | Temperatuur | Waarde | Conditie | Verwante normen | Commentaar |
|---|---|---|---|---|---|
| Coëfficiënt van thermische uitzetting | -50,0 °C | 2e-05 1/K | T5 | WL 3.2364 | |
| 100,0 °C | 2.14e-05 1/K | T5 | WL 3.2364 | ||
| 200,0 °C | 2.25e-05 1/K | T5 | WL 3.2364 | ||
| 300,0 °C | 2.33e-05 1/K | T5 | WL 3.2364 | ||
| Smeltpunt | 505.0 - 770,0 °C | Typisch voor gegoten aluminium uit de 3xx.x-serie | |||
| Specifieke warmtecapaciteit | 960,0 - 963,0 J/(kg·K) | Typisch voor gegoten aluminium uit de 3xx.x-serie | |||
| Thermische geleidbaarheid | 130,0 - 180,0 W/(m·K) | Typisch voor gegoten aluminium uit de 3xx.x-serie |
Chemische eigenschappen
| Eigendom | Waarde | Conditie | Verwante normen |
|---|---|---|---|
| Koper | 0.2 | T5 | WL 3.2364 |
| Strijkijzer | 0,6 | T5 | WL 3.2364 |
| Magnesium | 0,2 - 0,4 % | T5 | WL 3.2364 |
| Mangaan | 0,35 | T5 | WL 3.2364 |
| Silicium | 6,5 - 7,5 % | T5 | WL 3.2364 |
| Titanium | 0,25 | T5 | WL 3.2364 |
| Zink | 0,3 | T5 | WL 3.2364 |
Technologische eigenschappen
| Eigenschap | ||
|---|---|---|
| Verwerkingsmethoden | permanent gieten, monster genomen uit gieten
| |
Metaal