Roze bladen rang 356,0 T6
Eigenschappen
Algemeen
| Eigendom | Waarde | Conditie |
|---|---|---|
| Dichtheid | 2,7 g/cm³ | T6 |
Mechanisch
| Eigendom | Temperatuur | Waarde | Conditie | Verwante normen | Vorm | Commentaar |
|---|---|---|---|---|---|---|
| Druksterkte vloeigrens | 172,0 - 186,0 MPa | T6 | ||||
| Elastische modulus | 72,0 GPa | T6 | ||||
| 72,4 GPa | T6 | |||||
| Verlenging | -195 °C | 3,5 % | T6 | Zandgegoten, rek in 50 mm | ||
| -80 °C | 3,5 % | T6 | Zandgegoten, rek in 50 mm | |||
| -28 °C | 3,5 % | T6 | Zandgegoten, rek in 50 mm | |||
| 3,0 % | T6 | Roze platen, ASTM B108, ASTM B26, ASTM B618, ASTM B955 | Casten | A100 | ||
| 3,8 % | T6 | |||||
| 24 °C | 3,5 % | T6 | Zandgegoten, rek in 50 mm | |||
| 100 °C | 4 % | T6 | Zandgegoten, rek in 50 mm | |||
| 150 °C | 6 % | T6 | Zandgegoten, rek in 50 mm | |||
| 205 °C | 18 % | T6 | Zandgegoten, rek in 50 mm | |||
| 260 °C | 35 % | T6 | Zandgegoten, rek in 50 mm | |||
| 315 °C | 60% | T6 | Zandgegoten, rek in 50 mm | |||
| 371 °C | 80 % | T6 | Zandgegoten, rek in 50 mm | |||
| Vermoeidheidskracht | 90 MPa | T6 | voor 5x10⁸ cycli, R.R. Moore type test | |||
| Hardheid, Brinell | 70.0 [-] | T6 | Roze platen, ASTM B26, ASTM B618 | Casten | ||
| 80 [-] | T6 | 500 kg belasting, 10 mm b | ||||
| 85.0 [-] | T6 | Roze platen, ASTM B108, ASTM B955 | Casten | |||
| Poisson-verhouding | 0,33 [-] | T6 | ||||
| Afschuifmodulus | 27,2 GPa | T6 | ||||
| Schuifsterkte | 179 MPa | T6 | ||||
| Treksterkte | -195 °C | 275 MPa | T6 | Zandgegoten | ||
| -80 °C | 240 MPa | T6 | Zandgegoten | |||
| -28 °C | 227 MPa | T6 | Zandgegoten | |||
| 205,0 MPa | T6 | Roze platen, ASTM B26, ASTM B618 | Casten | |||
| 220,0 MPa | T6 | |||||
| 230,0 MPa | T6 | Roze platen, ASTM B108, ASTM B955 | Casten | |||
| 24 °C | 227 MPa | T6 | Zandgegoten | |||
| 100 °C | 220 MPa | T6 | Zandgegoten | |||
| 150 °C | 160 MPa | T6 | Zandgegoten | |||
| 205 °C | 83 MPa | T6 | Zandgegoten | |||
| 260 °C | 53 MPa | T6 | Zandgegoten | |||
| 315 °C | 28 MPa | T6 | Zandgegoten | |||
| 371 °C | 17 MPa | T6 | Zandgegoten | |||
| Opbrengststerkte | -195 °C | 193 MPa | T6 | Zandgegoten, RP02 | ||
| -80 °C | 172 MPa | T6 | Zandgegoten, RP02 | |||
| -28 °C | 165 MPa | T6 | Zandgegoten, RP02 | |||
| 140,0 MPa | T6 | Roze platen, ASTM B26, ASTM B618 | Casten | RP02 | ||
| 150,0 MPa | T6 | Roze platen, ASTM B108, ASTM B955 | Casten | RP02 | ||
| 170,0 MPa | T6 | |||||
| 24 °C | 165 MPa | T6 | Zandgegoten, RP02 | |||
| 100 °C | 165 MPa | T6 | Zandgegoten, RP02 | |||
| 150 °C | 138 MPa | T6 | Zandgegoten, RP02 | |||
| 205 °C | 58 MPa | T6 | Zandgegoten, RP02 | |||
| 260 °C | 35 MPa | T6 | Zandgegoten, RP02 | |||
| 315 °C | 21 MPa | T6 | Zandgegoten, RP02 | |||
| 371 °C | 14 MPa | T6 | Zandgegoten, RP02 |
Thermisch
| Eigendom | Temperatuur | Waarde | Conditie | Verwante normen | Vorm | Commentaar |
|---|---|---|---|---|---|---|
| Coëfficiënt van thermische uitzetting | 2.2e-05 1/K | T6 | ||||
| Smeltpunt | 557,0 - 613,0 °C | T6 | Roze platen, ASTM B108, ASTM B26, ASTM B618, ASTM B955 | Casten | ||
| 570,0 °C | T6 | |||||
| Specifieke warmtecapaciteit | 970,0 J/(kg·K) | T6 | ||||
| 100 °C | 960 J/(kg·K) | T6 | afgeleide waarde | |||
| Thermische geleidbaarheid | 150,0 W/(m·K) | T6 | ||||
| 25 °C | 150 W/(m·K) | T6 | afgeleide waarde |
Elektrisch
| Eigendom | Waarde | Conditie | Commentaar |
|---|---|---|---|
| Elektrische geleidbaarheid | 23000000 S/m | T6 | Typische/afgeleide waarden |
| Elektrische weerstand | 4.42e-08 ·m | T6 | Typische waarden |
| Specifieke elektrische geleidbaarheid | 39,0 - 41,0 % GBCS | T6 | Typische waarden |
Chemische eigenschappen
| Eigendom | Waarde | Conditie | Verwante normen | Vorm |
|---|---|---|---|---|
| Aluminium | 90,1 - 93,3% | T6 | ||
| Koper | 0,25% | T6 | Roze platen, ASTM B108, ASTM B26, ASTM B618, ASTM B955 | Casten |
| Strijkijzer | 0,6 % | T6 | ||
| 0,60 % | T6 | Roze platen, ASTM B108, ASTM B26, ASTM B618, ASTM B955 | Casten | |
| Magnesium | 0,2 - 0,45 % | T6 | Roze platen, ASTM B108, ASTM B26, ASTM B618, ASTM B955 | Casten |
| Mangaan | 0,35 % | T6 | Roze platen, ASTM B108, ASTM B26, ASTM B618, ASTM B955 | Casten |
| Andere | 0,15 % | T6 | ||
| Silicium | 6,5 - 7,5 % | T6 | Roze platen, ASTM B108, ASTM B26, ASTM B618, ASTM B955 | Casten |
| Titanium | 0,25% | T6 | Roze platen, ASTM B108, ASTM B26, ASTM B618, ASTM B955 | Casten |
| Zink | 0,35 % | T6 | Roze platen, ASTM B108, ASTM B26, ASTM B618, ASTM B955 | Casten |
Metaal