AA-normen klasse 1060 H18
Eigenschappen
Algemeen
| Eigendom | Waarde | Conditie | Verwante normen |
|---|---|---|---|
| Dichtheid | 2,705 g/cm³ | H18 | AA-normen, ASTM B209, ASTM B210, ASTM B483 |
Mechanisch
| Eigendom | Waarde | Conditie | Verwante normen | Commentaar |
|---|---|---|---|---|
| Buigen Vermoeidheid Kracht | 45,0 MPa | H18 | AA-normen | |
| Elastische modulus | 69,0 GPa | H18 | AA-normen, ASTM B209, ASTM B210, ASTM B483 | |
| Hardheid, Brinell | 35.0 [-] | H18 | AA-normen | |
| Plane-Strain Fracture Toughnes | 22,0 - 35,0 MPa·√m | Typisch voor gesmeed aluminium uit de 1000-serie | ||
| Poisson-verhouding | 0,33 [-] | Typisch voor gesmeed aluminium uit de 1000-serie | ||
| Afschuifmodulus | 25,9 GPa | Typisch voor gesmeed aluminium uit de 1000-serie | ||
| Treksterkte | 110,0 MPa | H18 | AA-normen, ASTM B209, ASTM B210, ASTM B483 | |
| 130,0 MPa | H18 | AA-normen |
Thermisch
| Eigendom | Temperatuur | Waarde | Conditie | Verwante normen | Commentaar |
|---|---|---|---|---|---|
| Coëfficiënt van thermische uitzetting | 20 °C | 2.36e-05 1/K | H18 | AA-normen, ASTM B209, ASTM B210, ASTM B483 | |
| 100 °C | 2.36e-05 1/K | H18 | AA-normen, ASTM B209, ASTM B210, ASTM B483 | ||
| Smeltpunt | 645,0 - 655,0 °C | H18 | AA-normen, ASTM B209, ASTM B210, ASTM B483 | ||
| Specifieke warmtecapaciteit | 900,0 - 963,0 J/(kg·K) | Typisch voor gesmeed aluminium uit de 1000-serie | |||
| Thermische geleidbaarheid | 230,0 - 234,0 W/(m·K) | H18 | AA-normen, ASTM B209, ASTM B210, ASTM B483 |
Elektrisch
| Eigendom | Waarde | Conditie | Verwante normen |
|---|---|---|---|
| Elektrische geleidbaarheid | 35000000,0 - 3000000,0 S/m | H18 | AA-normen, ASTM B209, ASTM B210, ASTM B483 |
| Elektrische weerstand | 2.78e-08 - 2.86e-08 ·m | H18 | AA-normen, ASTM B209, ASTM B210, ASTM B483 |
Chemische eigenschappen
| Eigendom | Waarde | Conditie | Verwante normen |
|---|---|---|---|
| Aluminium | 99,6% | H18 | AA-normen, ASTM B209, ASTM B210, ASTM B483 |
| Koper | 0,05% | H18 | AA-normen, ASTM B209, ASTM B210, ASTM B483 |
| Strijkijzer | 0,35 % | H18 | AA-normen, ASTM B209, ASTM B210, ASTM B483 |
| Magnesium | 0,03 % | H18 | AA-normen, ASTM B209, ASTM B210, ASTM B483 |
| Mangaan | 0,03 % | H18 | AA-normen, ASTM B209, ASTM B210, ASTM B483 |
| Silicium | 0,25% | H18 | AA-normen, ASTM B209, ASTM B210, ASTM B483 |
| Titanium | 0,03 % | H18 | AA-normen, ASTM B209, ASTM B210, ASTM B483 |
| Vanadium | 0,05% | H18 | AA-normen, ASTM B209, ASTM B210, ASTM B483 |
| Zink | 0,05% | H18 | AA-normen, ASTM B209, ASTM B210, ASTM B483 |
Technologische eigenschappen
| Eigenschap | ||
|---|---|---|
| Hardsolderen | algemeen:mogelijk met commerciële processen en methoden
| |
| Corrosie-eigenschappen | Spanningscorrosie:geen schade tijdens bedrijf en laboratoriumtests, algemeen:zeer goed, zonder bescherming in industriële of zeewateratmosfeer
| |
| Algemene bewerkbaarheid | Algemeen:niet geschikt (O, H12), slecht (H14, H16, H18)
| |
| Werkbaarheid | algemeen (staat):goed (O, H12, H14), acceptabel (H16, H18)
| |
Metaal