AA-normen klasse 5050 H38
Eigenschappen
Algemeen
| Eigendom | Waarde | Conditie | Verwante normen |
|---|---|---|---|
| Dichtheid | 2,69 g/cm³ | H38 | AA-normen, ASTM B209, ASTM B210, ASTM B313, ASTM B483 |
Mechanisch
| Eigendom | Waarde | Conditie | Verwante normen | Commentaar |
|---|---|---|---|---|
| Buigen Vermoeidheid Kracht | 95,0 MPa | H38 | AA-normen | |
| Elastische modulus | 69,0 GPa | H38 | AA-normen, ASTM B209, ASTM B210, ASTM B313, ASTM B483 | |
| Hardheid, Brinell | 63,0 [-] | H38 | AA-normen | |
| Plane-Strain Fracture Toughnes | 22,0 - 35,0 MPa·√m | Typisch voor gesmeed aluminium uit de 5000-serie | ||
| Poisson-verhouding | 0,33 [-] | Typisch voor gesmeed aluminium uit de 5000-serie | ||
| Afschuifmodulus | 26,0 - 26,5 GPa | Typisch voor gesmeed aluminium uit de 5000-serie | ||
| Treksterkte | 200,0 MPa | H38 | AA-normen, ASTM B209, ASTM B210, ASTM B313, ASTM B483 | |
| 220,0 MPa | H38 | AA-normen |
Thermisch
| Eigendom | Temperatuur | Waarde | Conditie | Verwante normen | Commentaar |
|---|---|---|---|---|---|
| Coëfficiënt van thermische uitzetting | 20 °C | 2.38e-05 1/K | H38 | AA-normen, ASTM B209, ASTM B210, ASTM B313, ASTM B483 | |
| 100 °C | 2.38e-05 1/K | H38 | AA-normen, ASTM B209, ASTM B210, ASTM B313, ASTM B483 | ||
| Maximale servicetemperatuur | 150,0 °C | Typisch voor gesmeed aluminium uit de 5000-serie | |||
| Smeltpunt | 625,0 - 650,0 °C | H38 | AA-normen, ASTM B209, ASTM B210, ASTM B313, ASTM B483 | ||
| Specifieke warmtecapaciteit | 879,0 - 963,0 J/(kg·K) | Typisch voor gesmeed aluminium uit de 5000-serie | |||
| Thermische geleidbaarheid | 193 W/(m·K) | H38 | AA-normen, ASTM B209, ASTM B210, ASTM B313, ASTM B483 |
Elektrisch
| Eigendom | Waarde | Conditie | Verwante normen |
|---|---|---|---|
| Elektrische geleidbaarheid | 29000000,0 S/m | H38 | AA-normen, ASTM B209, ASTM B210, ASTM B313, ASTM B483 |
| Elektrische weerstand | 3.45e-08 Ω·m | H38 | AA-normen, ASTM B209, ASTM B210, ASTM B313, ASTM B483 |
Chemische eigenschappen
| Eigendom | Waarde | Conditie | Verwante normen |
|---|---|---|---|
| Chroom | 0,1 % | H38 | AA-normen, ASTM B209, ASTM B210, ASTM B313, ASTM B483 |
| Koper | 0,2 % | H38 | AA-normen, ASTM B209, ASTM B210, ASTM B313, ASTM B483 |
| Strijkijzer | 0,70 % | H38 | AA-normen, ASTM B209, ASTM B210, ASTM B313, ASTM B483 |
| Magnesium | 1,1 - 1,8 % | H38 | AA-normen, ASTM B209, ASTM B210, ASTM B313, ASTM B483 |
| Mangaan | 0,1 % | H38 | AA-normen, ASTM B209, ASTM B210, ASTM B313, ASTM B483 |
| Silicium | 0,4 % | H38 | AA-normen, ASTM B209, ASTM B210, ASTM B313, ASTM B483 |
| Zink | 0,25% | H38 | AA-normen, ASTM B209, ASTM B210, ASTM B313, ASTM B483 |
Technologische eigenschappen
| Eigenschap | ||
|---|---|---|
| Hardsolderen | algemeen:Lötbar mit speziellen Techniken oder bei bestimmten Anwendungen
| |
| Corrosie-eigenschappen | Spanningscorrosie:geen schade tijdens bedrijf en laboratoriumtests, algemeen:zeer goed, zonder bescherming in industriële of zeewateratmosfeer
| |
| Algemene bewerkbaarheid | Algemeen:niet geschikt (O), slecht (H32, H34), voldoende (H36, H38)
| |
| Werkbaarheid | algemeen (conditie):goed (O, H32), acceptabel (H34), slecht (H36, H38)
| |
Metaal