AA-normen klasse 5154 H38
Eigenschappen
Algemeen
| Eigendom | Waarde | Conditie | Verwante normen |
|---|---|---|---|
| Dichtheid | 2,66 g/cm³ | H38 | AA-normen, ASTM B209, ASTM B211, ASTM B313 |
Mechanisch
| Eigendom | Waarde | Conditie | Verwante normen | Commentaar |
|---|---|---|---|---|
| Buigen Vermoeidheid Kracht | 145,0 MPa | H38 | AA-normen | |
| Elastische modulus | 70,0 GPa | H38 | AA-normen, ASTM B209, ASTM B211, ASTM B313 | |
| Hardheid, Brinell | 80,0 [-] | H38 | AA-normen | |
| Plane-Strain Fracture Toughnes | 22,0 - 35,0 MPa·√m | Typisch voor gesmeed aluminium uit de 5000-serie | ||
| Poisson-verhouding | 0,33 [-] | Typisch voor gesmeed aluminium uit de 5000-serie | ||
| Afschuifmodulus | 26,0 - 26,5 GPa | Typisch voor gesmeed aluminium uit de 5000-serie | ||
| Treksterkte | 310,0 MPa | H38 | AA-normen, ASTM B209, ASTM B211, ASTM B313 | |
| 330,0 MPa | H38 | AA-normen |
Thermisch
| Eigendom | Temperatuur | Waarde | Conditie | Verwante normen | Commentaar |
|---|---|---|---|---|---|
| Coëfficiënt van thermische uitzetting | 20 °C | 2.3899999999999998e-05 1/K | H38 | AA-normen, ASTM B209, ASTM B211, ASTM B313 | |
| 100 °C | 2.3899999999999998e-05 1/K | H38 | AA-normen, ASTM B209, ASTM B211, ASTM B313 | ||
| Maximale servicetemperatuur | 150,0 °C | Typisch voor gesmeed aluminium uit de 5000-serie | |||
| Smeltpunt | 590,0 - 645,0 °C | H38 | AA-normen, ASTM B209, ASTM B211, ASTM B313 | ||
| Specifieke warmtecapaciteit | 879,0 - 963,0 J/(kg·K) | Typisch voor gesmeed aluminium uit de 5000-serie | |||
| Thermische geleidbaarheid | 126 W/(m·K) | H38 | AA-normen, ASTM B209, ASTM B211, ASTM B313 |
Elektrisch
| Eigendom | Waarde | Conditie | Verwante normen |
|---|---|---|---|
| Elektrische geleidbaarheid | 19000000,0 S/m | H38 | AA-normen, ASTM B209, ASTM B211, ASTM B313 |
| Elektrische weerstand | 5.26e-08 ·m | H38 | AA-normen, ASTM B209, ASTM B211, ASTM B313 |
Chemische eigenschappen
| Eigendom | Waarde | Conditie | Verwante normen |
|---|---|---|---|
| Chroom | 0,15 - 0,35 % | H38 | AA-normen, ASTM B209, ASTM B211, ASTM B313 |
| Koper | 0,1 % | H38 | AA-normen, ASTM B209, ASTM B211, ASTM B313 |
| Strijkijzer | 0,40 % | H38 | AA-normen, ASTM B209, ASTM B211, ASTM B313 |
| Magnesium | 3,1 - 3,9 % | H38 | AA-normen, ASTM B209, ASTM B211, ASTM B313 |
| Mangaan | 0,1 % | H38 | AA-normen, ASTM B209, ASTM B211, ASTM B313 |
| Silicium | 0,25% | H38 | AA-normen, ASTM B209, ASTM B211, ASTM B313 |
| Titanium | 0,2 % | H38 | AA-normen, ASTM B209, ASTM B211, ASTM B313 |
| Zink | 0,2 % | H38 | AA-normen, ASTM B209, ASTM B211, ASTM B313 |
Technologische eigenschappen
| Eigenschap | ||
|---|---|---|
| Hardsolderen | algemeen:er is geen hardsolderen bekend of ontwikkeld
| |
| Corrosie-eigenschappen | Spanningscorrosie:geen schade tijdens bedrijf en laboratoriumtests, algemeen:zeer goed, zonder bescherming in industriële of zeewateratmosfeer
| |
| Algemene bewerkbaarheid | Algemeen:matig (O, H32), voldoende (H34, H36, H38)
| |
| Werkbaarheid | algemeen (conditie):goed (O), acceptabel (H32, H34), slecht (H36, H38)
| |
Metaal